Hi, All,
We have Rigaku, smartlab x-ray defractometer. But we have some problem to
run it now like below:
We initially had issues with the sample alignments where the peaks were
outside of the typical range. Before the problem was fixed, we ran optical
alignments and changed the slits once or twic
We have Rigaku, smartlab x-ray defractometer. But we have some problem to
run it now like below:
We initially had issues with the sample alignments where the peaks were
outside of the typical range. Before the problem was fixed, we ran optical
alignments and changed the slits once or twice. Once th
-- Forwarded message --
From: 최종락
Date: Thu, Jul 12, 2018 at 10:17 AM
Subject: Re: XRD on cotton yarn
To: Edward Laitila
Ed,
Thank you for your input for me.
So, as for the area prep., 1mm thick should be enough? and I will try to
cut the area again that I have done it before
Dear All,
Hi, how are you, guys.
My name is Jonglak choi, who is working on obtaining quantity of
crystalline through CI(%)-cyrstal index for natural cotton (cellulose type
I). We have Rigaku XRD instrument for obtaining defraction pattern from the
cotton yarns. In order to know about the quantity
Hi~,
Although I am out of the track to do chemistry for now, I am still happy to
be in the list to feel a chemist.
And the patterns are same for me with just small bit of Zero shift. I am
curious what they made out of it.
CJ
On Fri, May 8, 2015 at 11:45 AM, Leopoldo Suescun
wrote:
> Dear colle