I squeeze the T-88 hardener onto a flat surface "pallet" that I am going to mix it on. Then beside it, I squeeze the resin. I try to get the same diameter and height circle for each. I do the hardener first because it settles slower. I have even drawn circles on the pallet to give me something to go by.
The part should break, not the glue. Remember that if you squeeze the parts together too tight and have too smooth a surface, you will not get as good a bond. Squeezing too tight just squeezes the T-88 out of the joint. Don't take this as the "correct" bonding process, it is just the best way I have found to work with T-88. See you in Mt. Vernon - 2006 - KR Gathering See N64KR at http://KRBuilder.org - Then click on the pics There is a time for building and a time for FLYING and the time for building has expired. Daniel R. Heath - Columbia, SC -------Original Message------- Can someone tell me if my bonding process is correct???? what sort of processess do people use to mix there t-88 in correct proportions??