I need some advice on T-88 glue joints. I have a disc sander made from a
wood lathe, which I use to get a perfect fit between parts, then coat both
mating surfaces with T-88, and apply light pressure, I kept a sample of the
epoxy, and a sample glue joint, which broke along the grain of the wood when
tested. Can someone tell me if my bonding process is correct???? The sample
epoxy set like epoxy should, although I have not been able to get a consistant
opinion on what to do with it, some say break it and others say it is next to
useless for testing purposes, and if you do break it, what do you look for?? I
am pretty sure what I have done is correct, but It would pay to make sure that
the process is 100 per cent done the right way. This may sound a bit silly, but
what sort of processess do people use to mix there t-88 in correct proportions??