Right on Mark. 4130 is an air hardening alloy, and can get harder than a > file if cooled quickly, and it would be. > > Heat treating is inexpensive, and would be easy for a WAF set, especially in > quantity.
During the switch I don't know if you got my response to this post. So here it is again: You made a believer of me , and reminded me of a job I did using 4130 Shaft. It was all I had so I thought what the Heck. Problem was it hat to be tack welded to the conveyor rollers, the quick cooling hardened it to the point the shaft snapped when bumped. With that in mind, Mark L. didn't you have your panel water jet cut? This should be a very cool process. How 'bout it? Leigh Plymale flyboy...@adelphia.net -------------- next part -------------- An HTML attachment was scrubbed... URL: http://mylist.net/private/krnet/attachments/20030409/6d236756/attachment.htm